Silíkon rtv sprautu svart 200ml 0893 331 1
|
Black |
1x |
|
Vörunúmer: 0893 331 1
-
Contents
200 ml
-
Colour
Black
-
Chemical basis
Neutral crosslinked silicones, oxime-based
-
Min. skin-formation time
5 min
-
Fully hardening/curing conditions
23°C and 50% relative humidity
-
Shore A hardness
30
-
Min. tensile strength
2.2 N/mm²
-
Conditions for tensile strength
in accordance with ASTM D-412
-
Conditions for specific volume resistivity
in accordance with ASTM D-257
-
Min./max. temperature resistance
-60 to 260 °C
|
Silíkon rtv sprautu rautt 200ml 0893 331 2
|
Red |
1x |
|
Vörunúmer: 0893 331 2
-
Contents
200 ml
-
Colour
Red
-
Chemical basis
Neutral crosslinked silicones, oxime-based
-
Min. skin-formation time
5 min
-
Fully hardening/curing conditions
23°C and 50% relative humidity
-
Shore A hardness
25
-
Min. tensile strength
2.2 N/mm²
-
Conditions for tensile strength
in accordance with ASTM D-412
-
Conditions for specific volume resistivity
in accordance with ASTM D-257
-
Min./max. temperature resistance
-60 to 315 °C
|
Silíkon rtv sprautu glært 200ml 0893 331 4
|
Transparent |
1x |
|
Vörunúmer: 0893 331 4
-
Contents
200 ml
-
Colour
Transparent
-
Chemical basis
Neutral crosslinked silicones, oxime-based
-
Min. skin-formation time
5 min
-
Fully hardening/curing conditions
23°C and 50% relative humidity
-
Shore A hardness
26
-
Min. tensile strength
2.2 N/mm²
-
Conditions for tensile strength
in accordance with ASTM D-412
-
Conditions for specific volume resistivity
in accordance with ASTM D-257
-
Min./max. temperature resistance
-60 to 260 °C
|
Silíkon rtv sprautu grátt 200ml 0893 331 6
|
Grey |
1x |
|
Vörunúmer: 0893 331 6
-
Contents
200 ml
-
Colour
Grey
-
Chemical basis
Neutral crosslinked silicones, oxime-based
-
Min. skin-formation time
5 min
-
Fully hardening/curing conditions
23°C and 50% relative humidity
-
Shore A hardness
26
-
Min. tensile strength
2.2 N/mm²
-
Conditions for tensile strength
in accordance with ASTM D-412
-
Conditions for specific volume resistivity
in accordance with ASTM D-257
-
Min./max. temperature resistance
-60 to 260 °C
|